TA2 Titanium Alloy Pipe，Compared with other metal materials, it has the following advantages: 1. High specific strength (tensile strength/density) (see figure), the tensile strength can reach 100 ~ 140kgf/mm2, while the density is only 60% of steel. 2. The medium temperature strength is good, the use temperature is several hundred degrees higher than aluminum alloy, in the medium temperature can still maintain the required strength, can work in 450 ~ 500℃ temperature for a long time. 3. Good corrosion resistance, titanium surface in the atmosphere immediately formed a layer of uniform and dense oxide film, has the ability to resist a variety of media erosion. Titanium generally has good corrosion resistance in oxidizing and neutral media, especially in seawater, wet chlorine and chloride solutions. But in reducing medium, such as hydrochloric acid solution, titanium corrosion resistance is poor. 4. Titanium alloys with good low temperature performance and very low clearance elements, such as TA7, can maintain certain plasticity at -253℃. 5. Low elastic modulus, small thermal conductivity, no ferromagnetism. 6. High hardness. 7. Poor stamping property and good thermoplasticity. Heat treatment Titanium alloy can obtain different phase composition and microstructure by adjusting heat treatment process. It is generally considered that fine equiaxed microstructure has good plasticity, thermal stability and fatigue strength. The acicular structure has higher durable strength, creep strength and fracture toughness. Equiaxed and acicular mixed structures have better comprehensive properties. TA2 Titanium Alloy Pipe, The commonly used heat treatment methods are annealing, solution and aging treatment. Annealing is to eliminate internal stress, improve plasticity and microstructure stability, in order to obtain better comprehensive properties. Generally, the annealing temperature of α alloy and (α+β) alloy is 120 ~ 200℃ below the transition point of (α+β) -- →β phase. The solution and aging treatment is to obtain the α 'phase and the metastable β phase of martensite by fast cooling in the high temperature region, and then decompose these metastable phases by holding in the middle temperature region, and obtain the fine dispersed second phase particles, such as α phase or compound, to achieve the purpose of strengthening the alloy. Usually (alpha + beta) alloy quenching in alpha + beta) -- - > beta phase transition point below 40 ~ 100 ℃, metastable beta alloy quenching in alpha + beta) -- - > beta phase transition point above 40 ~ 80 ℃. The aging temperature is generally 450 ~ 550℃. In addition, in order to meet the special requirements of the workpiece, the industry also uses double annealing, isothermal annealing, β heat treatment, deformation heat treatment and other metal heat treatment process.Titanium pipe, titanium welding pipe, titanium splicing tee, titanium splicing elbow, titanium welding ring, titanium reducing, titanium tee, titanium elbow, titanium chimney, etc.TA2 Titanium Alloy Pipe, Mainly connecting all kinds of titanium equipment pipeline, used for material circulation between all kinds of equipment, the pipeline has the corrosion resistance of titanium material itself, so as to replace the general pipeline for ordinary pipeline can not meet the demand. Generally ф 108 above are welded pipes.

DN（mm）	Measuring the outer diameter（mm）	The material
15	18	TA2
20	25	TA2
25	32	TA2
32	38	TA2
40	45	TA2
50	57	TA2
65	76	TA2
80	89	TA2
100	108	TA2
125	133	TA2
150	159	TA2
200	219	TA2
250	273	TA2
300	325	TA2
350	377	TA2
400	426	TA2
450	480	TA2
500	530	TA2
600	630	TA2