Aluminium 1050 Plate，Belt belongs to a product of pure aluminum plate series, and the chemical composition and mechanical properties of 1060 series products are nearly the same, and the application is basically replaced by 1060 aluminum plate belt. The last two digits in the 1050 series are 50. According to the naming principle of international brand, the aluminum content must reach 99.5% or more for qualified products. China's aluminum alloy technical standard (GB/T3880-2006) also clearly stipulates that the aluminum content of 1050 reaches 99.5%. Because it does not contain other technical elements, the production process is relatively simple and the price is relatively cheap. It is the most commonly used series in conventional industry. Industrial pure aluminum has high plasticity, corrosion resistance, electrical conductivity and good thermal conductivity, but low strength, not through heat treatment to strengthen, machinability is not good, can accept contact welding, gas welding.Industrial pure aluminum has the general characteristics of aluminum, small density, good electrical and thermal conductivity, good corrosion resistance, good plastic processing performance, can be processed into plates, belts, foil and extruded products, can be gas welding, argon arc welding, spot welding. Industrial pure aluminum can not be strengthened by heat treatment, can improve the strength through cold deformation, the only form of heat treatment is annealing, recrystallization start temperature and impurity content and deformation degree, generally about 200℃. σ B= 80 ~ 100MPa, σ0.2=30 ~ 50MPa, ζ=35% ~ 40%, HB=25 ~ 30. After 60%-80% cold deformation, the ζ value decreases to 1%-1.5%, although the ζ value increases to 150-180mpa. Increasing the content of fe and Si impurities can improve the strength, but reduce the plasticity, electrical conductivity and corrosion resistance. The mechanical properties of 1200(L5) industrial pure aluminum sheet under different hardening conditions can be obtained by adjusting the annealing temperature after cold deformation or controlling the cold deformation after annealing. In order to improve formability, it is better to adopt the former method.Aluminium 1050 Plate, Used in daily necessities, lighting appliances, reflective panels, decorations, chemical industry containers, radiators, signs, electronics, lamps, nameplates, electrical appliances, stamping parts and other products. In some requirements of corrosion resistance and formability are high occasions, but the strength is not high, chemical equipment is its typical use.Tensile strength σ B (MPa) : 60 ~ 100 Elongation δ/ (%) : ≥23 Elongation 50mm/ (%) : ≥25 Note: Longitudinal mechanical properties of pipe at room temperature Sample size: all wall thicknesses Heat treatment specification: 1) Complete annealing: heating 390 ~ 430℃; The insulation time is 30 ~ 120min depending on the effective thickness of the material. At the speed of 30 ~ 50℃/h, the furnace is cooled to 300℃, and then air cooled. 2) Rapid annealing: heating 350 ~ 370℃; The insulation time is 30 ~ 120min depending on the effective thickness of the material. Air or water cooling. 3) Quenching and aging: quenching 500 ~ 510℃, air cooling; Artificial aging 95 ~ 105℃,3h, air cooling; Natural aging room temperature 120h

Alloy	Si	Fe	Cu	Mn	Mg	Cr		Ni	Zn		Ti	Other		Al
												Single	Total
1060	0.25	0.35	0.05	0.03	0.03	_		_	0.05	V:0.05	0.03	0.03	_	99.6
1050	0.25	0.4	0.05	0.05	0.05	_		_	0.05	V:0.05	0.03	0.03	_	99.5
1100	Si+Fe:0.95		0.05~0.40	0.05	_	_		_	0.1	_	_	0.05	0.15	99
1200	Si+Fe:1.00		0.05	0.05		_		_	0.1	_	0.05	0.05	0.15	99
3003	0.6	0.7	0.05~0.20	1.0~1.5	_	_		_	0.1		_	0.05	0.15	R
3004	0.3	0.7	0.25	1.0~1.5	0.8~1.3	_		_	0.25		_	0.05	0.15	R
3005	0.6	0.7	0.3	1.0~1.5	0.20~0.6	0.1		_	0.25		0.1	0.05	0.15	R
3105	0.6	0.7	0.3	0.30~0.8	0.20~0.8	0.2		_	0.4		0.1	0.05	0.15	R
5005	0.3	0.7	0.2	0.2	0.50~1.1	0.1		_	0.25	_	_	0.05	0.15	R
5052	0.25	0.4	0.1	0.1	2.2~2.8	0.15~0.35		_	0.1	_	_	0.05	0.15	R
5083	0.4	0.4	0.1	0.40~1.0	4.0~4.9	0.05~0.25		_	0.25	_	0.15	0.05	0.15	R
5086	0.4	0.5	0.1	0.20~0.7	3.5~4.5	0.05~0.25		_	0.25	_	0.15	0.05	0.15	R

Product Name	Aluminum Alloy Plate
Aluminum Alloy	1000 Series: 1050 1060 1070 1100 1200 1235 etc. 2000 Series: 2A12 2014 2024 etc. 3000 Series: 3003 3004 3005 3104 3105 3A21 etc. 4000 Series: 4045 4047 4343 etc. 5000 Series: 5005 5052 5083 5086 5154 5182 5251 5754 etc. 6000 Series: 6061 6063 6082 6A02 etc. 7000 Series: 7050 7475 7075 etc. 8000 Series: 8011 8079 etc.
Temper	O, H12, H14, H16, H18, H22, H24, H26, H32, H112, T3, T4, T5, T6, T7, T8
Thickness	0.1mm - 260mm
Width	500-2000mm
Length	to clients' requirement
Coating	Polyester, Fluorocarbon, polyurethane and epoxy coating
Surface	Mill finished, Coated, Embossed,Brushed, Polished, Mirror, Anodized,etc
Gloss	Meet the customer requirement
Material	Aluminum Alloy Metal
Standard	GB/T3190-2008,GB/T3880-2006,ASTM B209,JIS H4000-2006,etc
OEM service	Perforated, Cutting special size, Doing flatness, Surface treatment,etc
Usage	Construction filed, Ships building industry, Decoration, Industry,Manufacture,Machinery and hardware fields, etc
Delivery	In general, within 7-15 working days after receiving deposit or According to Final order quantity
Packaging Details	Standard export package. One pallet is about 2-3 ton.Two steel belts in width and three in width. One 20GP container can load about 18-20 tons Aluminium 6061 Sheet. One 40GP container can load about 24 tons Aluminium 6061 Sheet